This is a Bismuth based Eutectic low melting alloy used for tooling and production aids. It provides you with easily castable material that is ready for use as soon as it freezes. This alloy can be recovered easily and recycled into new uses a number of times. It is mainly used in the optical industry for lens blocking when grinding glass, plastic lenses and optical components. It’s low melting point allows it not to distort the glass or plastic which it supports. Also can be used for proof casting as well.

Forms:
  • 2 lb Cake Even Weight
Belmont Product Code 2451
Nominal Composition:
  • 44.7% Bi
  • 5.3% Cd
  • 22.6% Pb
  • 19.1% In
  • 8.3% Sn
Technical Info:
  • Melting Point - Solidus 117 F, 47 C
  • Melting Point - Liquidus 117 F, 47 C
  • Short-Term Tensile Strength lbs/sq.in. 5400
  • Yield Temperature 117
  • Weight lbs/cu.in 0.32
  • Brinnell Hardness No. (500 kg) 12
  • Growth/Shrinkage - Time after Casting: after 2 mi.: 0.0005
  • after 1 hour: -0.0001
  • after 24 hrs: -0.0002
  • after 500 hrs: -0.0002

Related products

  •  
     
    BEND Metal, 158 F, 70 C Low Melting Alloy
    BEND Metal, 158 F, 70 C Low Melting Alloy

    This is a Bismuth based Eutectic low melting alloy used very often to bend tubes and rolled or extruded shapes. This alloy which is normally used for tubes up to 2-1/2″ Diameter allows them to be bent or formed to the desired shape without any kinks. Without using this material the tubes or shapes may kink or bend irregularly. It can also be used for work-holding, fusible safety devices and low temperature soldering.

    Forms:
    • Cakes
    • Capping Bars
    • 1/8" & Down Shot
    • .05", 1/8", 3/32" Dia Solid Wire
    • 1/8" x 18" Cast Strips
    Belmont Product Code 2505
    Nominal Composition:
    • 50% Bi
    • 10% Cd
    • 26.7% Pb
    • 13.3% Sn
    Technical Info:
    • Melting Point - Solidus 158 F, 70 C
    • Melting Point - Liquidus 158 F, 70 C
    • Short-Term Tensile Strength lbs/sq.in. 5990
    • Yield Temperature 158
    • Weight lbs/cu.in 0.339
    • Brinnell Hardness No. (500 kg) 9.2
    • Growth/Shrinkage - Time after Casting: after 2 mi.: 0.0025
    • after 1 hour: 0.0051
    • after 24 hrs: 0.0051
    • after 500 hrs: 0.0057
  •  
     
    CAST Metal, 281-338 F, 138-170 C Low Melting Alloy
    CAST Metal, 281-338 F, 138-170 C Low Melting Alloy

    This is a Tin based non-eutectic low melting alloy . The principle uses of this alloy are in applications similar to investment casting in which it substitutes for the so called ” lost wax ” pattern dies. It’s other applications also include proof casting and sealing or soldering in low-temperature applications.

    Forms:
    • Cakes
    • Slug
    Belmont Product Code 2405
    Nominal Composition:
    • 40% Bi
    • 60% Sn
    Technical Info:
    • Melting Point - Solidus 281 F, 138 C
    • Melting Point - Liquidus 338 F, 170 C
    • Short-Term Tensile Strength lbs/sq.in. 8000
    • Yield Temperature 302
    • Weight lbs/cu.in 0.296
    • Brinnell Hardness No. (500 kg) 22
    • Growth/Shrinkage - Time after Casting: after 2 mi.: -0.0001
    • after 1 hour: -0.0001
    • after 24 hrs: -0.0001
    • after 500 hrs: -0.0001
  •  
     
    136 F, 58 C Low Melting Alloy
    136 F, 58 C Low Melting Alloy

    This is a Bismuth based Eutectic low melting alloy used for tooling and production aids. It provides you with easily castable material that is ready for use as soon as it freezes. This alloy can be recovered easily and recycled into new uses a number of times. It is mainly used in the optical industry for lens blocking when grinding glass, plastic lenses and optical components. It’s low meeting point allows it not to distort the glass or plastic which it supports, Also can be used for proof casting as well. In comparison to its 117 Deg F. counterpart this alloy does not contain Cadmium.

    Forms:
    • 2 Lb. Cake Even Weight
    • 1/8" Dia Solid Wire
    • Capping Bars
    Belmont Product Code 2491
    Nominal Composition:
    • 49% Bi
    • 18% Pb
    • 21% In
    • 12% Sn
    Technical Info:
    • Melting Point - Solidus 136 F, 58 C
    • Melting Point - Liquidus 136 F, 58 C
    • Short-Term Tensile Strength lbs/sq.in. 6300
    • Yield Temperature 136
    • Weight lbs/cu.in 0.31
    • Brinnell Hardness No. (500 kg) 14
    • Growth/Shrinkage - Time after Casting: after 2 mi.: 0.0003
    • after 1 hour: 0
    • after 24 hrs: -0.0002
    • after 500 hrs: -0.0002

RELATED POSTS

Advantages of Eutectic Alloys vs. Non-Eutectic Alloys to Low Melting Materials

Eutectic alloys and non-eutectic alloys are categories when discussing low melting alloys. Low melting alloys require lower temperature ranges to melt, anywhere from 40 degrees to 300 degrees Fahrenheit. This property allows for the alloys to be melted at lower temperatures without damaging or impacting other nearby materials or surfaces that the low melting alloy…

Applications for Indium-Containing Low Melting Alloys

Low melting alloys are commonly used throughout the manufacturing process to help create products or placed inside of products for a specific function. These alloys melt and flow at very low temperatures depending on the composition of the base metals and additive metals. A common low melting base metal may consist of bismuth at higher…

Pure Bismuth: Characteristics of This Metal

Bismuth is an element that we often hear about in offhand ways yet don’t know a lot about at first. It is a crystalline element that comes in various colors ranging in white, purple, pink and silver. In its pure form, people will often think it is lead. Bismuth is widely used in the manufacturing…

Different Properties of Low Melting Alloys

Joining metal parts together with solder, easily bending pipes to go around corners and components, and lens blocking systems all rely on the use of low melting alloys. This type of metal allows for products, parts and components to be manufactured and cast at lower temperatures. This feature is ideal when requiring lower temperatures to…

Bismuth-Based Low Melting Alloys Providing Benefits to the Art Casting Industry

Throughout history, art casting has been used to create beautiful works of art, to recreate previous works of art that may have become damaged or deteriorated due to age, or when mass-producing art pieces. The art casting method involves using wood, stone, plaster, or silicon rubber molds and some type of pliable material, such as…

Low-Melting Alloys Containing Indium: Characteristics and Applications

Often when thinking about metal alloys, we consider the strength and durability of the metal to withstand a range of loads, stresses and extreme temperatures. Yet there are a range of manufacturing applications where an alloy needs to have a low melting characteristic. A low-melting alloy, also called fusible alloy, can take a liquefied or…

Applications Using Low Melting Alloys

Low melting alloys are considered fusible alloys because they melt at temperatures below 300 degrees are often combined with other metals in order to increase certain properties. For example, Bismuth is often combined with tin and/or silver to create lead-free solders that are non-toxic. Low Melting Alloy Applications and Uses Low melting alloys can be…

Benefits of Minor Metals for Your Manufacturing Business

Using minor metals from Belmont Metals in Brooklyn, NY can greatly improve your manufacturing process. These metals are often added to master alloys to improve certain desirable properties. For example, electrolytic manganese is often added to steel, aluminum and copper master alloys in order to increase the metal’s ferromagnetic properties. Types of Minor Metals and…

Characteristics of Low Melting Alloys

Manufacturers around the globe rely on quality materials to create a range of parts, equipment and products for businesses and consumers. During the assembly process, different materials may need to be joined together for a tight seal, cast in a mold to a designed form, or bent into a new direction without collapsing. Low melting…

Liquid metal’s low melting point

Fusible alloys’ low melting point makes them useful in a wide variety of applications The melting point of aluminum is 1,220 degrees Fahrenheit. Carbon steel melts somewhere between 2,600 and 2,800 degrees Fahrenheit, and the temperature needs to rise all the way up to 6,150 degrees Fahrenheit to melt tungsten. Specialized furnaces are needed to…

The Basics of Bismuth

This white element is an essential part of many alloys Purple-Silver, crystalline Bismuth has been in use since the early days of alloying, although during those times, it was often mistaken for Lead. It’s the most naturally diamagnetic element, which means it repels both north and south, and it has one of the lowest values…