Showing all 11 results
Featured products
-
Silicon ranks second to Copper in the importance in Aluminum Casting Alloys. Silicon reduces the melting temperature without causing brittleness, increases fluidity, and reduces hot tearing. This improves overall casting characteristics allowing for thinner and more intricate castings to be made. Silicon additions can reduce the amount casting shrinkage and in general Aluminum-Silicon Alloys have been resistance to corrosion. Forms: - 16-17 Waffle
- 30-60 Mesh Granular
Belmont Product Code 1503 Nominal Composition: - 50% Al
- 50% Si
Technical Info: - Melting Point (Liquidus): ~1,960°F (1,070°C)
- Melting Point (Solidus): ~1,070°F (577°C)
- Density: ~0.088 lbs/in³ (2.45 g/cm³)
- Solubility: Excellent in molten Aluminum at 1350°F+
-
Addition of small amounts of Beryllium appreciably resists oxidation in both the liquid and solid states. Forms: - 4-5 oz. pcs.
- 5 Lb. Slabs
Belmont Product Code 1978 Nominal Composition: - 94.75% Al
- 5.25% Be
Technical Info: - Melting Point (Liquidus): ~1,250°F (677°C)
- Melting Point (Solidus): ~1,190°F (643°C)
- Density: ~0.097 lbs/in³ (2.69 g/cm³)
- Solubility: Rapid in molten Aluminum/Magnesium at 1300°F+
-
Addition of small amounts of Beryllium appreciably resists oxidation in both the liquid and solid states. Forms: - 4-5 oz. pcs.
- 5 Lb. Slabs
Belmont Product Code 19516 Nominal Composition: - 94.75% Al
- 5.25% Be
Technical Info: - Melting Point (Liquidus): ~1,292°F (700°C)
- Melting Point (Solidus): ~1,191°F (644°C)
- Density: ~0.095 lbs/in³ (2.64 g/cm³)
- Solubility: Rapid dissolution in Aluminum at 1280°F - 1450°F
-
Lithium added to Alloys containing Magnesium help prevent dross formation. Forms: - 1" x 6" X 12" Slabs
- 2-2 Ingot
Belmont Product Code 19515 Nominal Composition: - 95% Al
- 5% Li
Technical Info: - Melting Point (Liquidus): ~1,185°F (640°C)
- Melting Point (Solidus): ~1,112°F (600°C)
- Density: ~0.083 lbs/in³ (2.30 g/cm³)
- Solubility: Rapid dissolution in molten Aluminum at 1300°F+
-
Chromium will improve strength without adversely affecting ductility. Forms: - 1" x 6" x 12" Slabs
Belmont Product Code 18012 Nominal Composition: - 80% Al
- 20% Cr
Technical Info: - Melting Point (Liquidus): ~1,920°F (1,050°C)
- Melting Point (Solidus): ~1,220°F (660°C)
- Density: ~0.111 lbs/in³ (3.08 g/cm³)
- Solubility: Good in molten Aluminum at 1350°F+
-
Magnesium improves the mechanical, fabrication, and welding characteristics of aluminum when used as an alloying agent. Forms: - 2"-1/4" Lumps
Belmont Product Code 6501B Nominal Composition: - 50% Al
- 50% Mg
Technical Info: - Melting Point (Liquidus): ~870°F (465°C)
- Melting Point (Solidus): ~842°F (450°C)
- Density: ~0.080 lbs/in³ (2.22 g/cm³)
- Solubility: Excellent dissolution in Aluminum at 1250°F+
-
Titanium is a grain refiner for Aluminum and improves mechanical properties. Forms: - 1" x 1" x 3" Sheared Pieces
Belmont Product Code 19512 Nominal Composition: - 94% Al
- 6% Ti
Technical Info: - Melting Point (Liquidus): ~2,012°F (1,100°C)
- Melting Point (Solidus): ~1,220°F (660°C)
- Density: ~0.099 lbs/in³ (2.75 g/cm³)
- Solubility: Good dissolution in Aluminum at 1350°F+
-
The presence of Iron in Aluminum aides in the decrease of hot tears, improves tensile, yield, and hardness and preserves strength at elevated temperature. Forms: - 16-20 Waffle
Belmont Product Code 1702 Nominal Composition: - 70 Al
- 30 Fe
Technical Info: - Melting Point (Liquidus): ~2,060°F (1,125°C)
- Melting Point (Solidus): ~1,220°F (660°C)
- Density: ~0.119 lbs/in³ (3.30 g/cm³)
- Solubility: Good in molten Aluminum at 1375°F+
-
The presence of Iron in Aluminum aides in the decrease of hot tears, improves tensile, yield, and hardness and preserves strength at elevated temperature. Forms: - 16-20 Waffle
Belmont Product Code 19013 Nominal Composition: - 90% Al
- 10% Fe
Technical Info: - Melting Point (Liquidus): ~1,580°F (860°C)
- Melting Point (Solidus): ~1,211°F (655°C)
- Density: ~0.103 lbs/in³ (2.85 g/cm³)
- Solubility: Excellent / Rapid in Aluminum at 1300°F+
-
Nickel adds hardness and strength. It improves machinability and helps retain high strength at elevated temperatures. Forms: - 1" x 6" x 12" Slabs
Belmont Product Code 1803 Nominal Composition: - 80% Al
- 20% Ni
Technical Info: - Melting Point (Liquidus): ~1,525°F (830°C)
- Melting Point (Solidus): ~1,184°F (640°C)
- Density: ~0.113 lbs/in³ (3.14 g/cm³)
- Solubility: Good in molten Aluminum at 1400°F+
-
Manganese added to Aluminum increases strength and hardness. It's beneficial in regards to corrosion resistance. Manganese is a grain refiner foir Aluminum. When Manganese is balanced with Iron it can change Iron rich needles to plates increasing ductility. Forms: - 5" x 1/2" Broken Slab
Belmont Product Code 1402 Nominal Composition: - 40% Al
- 60% Mn
Technical Info: - Melting Point (Liquidus): ~2,050°F (1,120°C)
- Melting Point (Solidus): ~1,220°F (660°C)
- Density: ~0.158 lbs/in³ (4.37 g/cm³)
- Solubility: Dissolution-driven at 1350°F+ (Does not melt instantly)