Low Melting (Fusible) Alloys

Featuring 158°F, 203°F radiation shielding alloys, pipe bending alloys, and low temperature solders. Eutectic: melting points from 117° – 281°F.Non-eutectic: melting points from 107° – 338°F.Mellottes metal, Rose metal, Wood’s metal, and others. Low-melting alloy wire.

Low-Melting or Fusible alloys (Also known as Eutectic and Non-Eutectic Alloys) are generally the alloys that melt below 450 Deg. F. ( 233 Deg. C ). The most useful are the alloys containing high percentages of Bismuth combined with Lead, Tin, Cadmium, Indium and other metals. The low melting temperature and unique growth/shrinkage characteristics of these alloys lead to a greater diversity in useful applications than almost any other alloy system.

Applications:

From radiation therapy shielding applications to creating chucks for holding parts during machining , from being used as filler material when bending pipe or tube to creating fusible elements in automatic fire sprinklers , Low-Melting alloys continue to have a quiet yet profound impact on our lives.

Forms:

Cake, Ingot, Bar, Shot, Wire, Stick, Strip & Custom Shapes

Featured Product Specifications

Open in Popup
Belmont
Product
Code
Industry
Designation
Melting
Point
-
Solidus
Melting
Point
-
Liquidus
Nominal
Composition
Short-Term
Tensile
Strength
lbs/sq.in.
Yield
Temperature
Weight
lbs/cu.in
Brinnell
Hardness
No.
(500
kg)
Growth/Shrinkage
-
Time
after
Casting
- - F C F C Bi Pb Sn Cd Others - F - - After 2 Min After 1 hr. After 24 hr After 500 hr
2451 LOW 117 117 47 117 47 44.70% 22.60% 8.30% 5.30% In 19.1% 5400 117 .32 12.0 +.0005 -.0001 -.0002 -.0002
2491 LOW 136 136 58 136 58 49% 18% 12% - In 21% 6300 136 .31 14.0 +.0003 .0000 -.0002 -.0002
2505 BEND 158 70 158 70 50% 26.70% 13.30% 10% - 5990 158 .339 9.2 +.0025 +.0051 +.0051 +.0057
2502 WOODS 158 70 169 76 50% 25% 12.50% 12.50% - 6100 158 .347 9.3 -.0001 +.0002 +.0031 +.0035
2431 SAFE 160 71 190 88 42.50% 37.70% 11.30% 8.50% - 5400 162.5 .341 9.0 -.0004 .0000 +.0022 +.0025
2531 MELLOTTES 203 95 203 95 52.50% 32% 15.50% - - 6100 203 .350 9.0 -.0002 +.0055 +.0057 +.0061
2503 ROSE 203 95 239 115 50% 25% 25% - - 6200 203 .3365 9.5 -.0001 +.0045 +.0052 +.0060
2481 MATRIX 218 103 440 227 48% 28.50% 14.50% - Sb 9.0% 13000 240 .343 19.0 +.0008 +.0048 +.0051 +.0061
2562 BASE 255 124 255 124 55.50% 44.50% - - - 6400 255 .38 10.2 -.0008 -.0008 +.0008 +.0022
2581 TRU 281 138 281 138 58% - 42% - - 8000 281 .315 22.0 +.0007 +.0006 +.0005 +.0005
2405 CAST 281 138 338 170 40% - 60% - - 8000 302 .296 22.0 -.0001 -.0001 -.0001 -.0001