Showing all 18 results
Featured products
-
Our standard Grade A Tin is sourced from highest quality supplier and is certified conflict free. We offer this material in a wide variety of forms so we can tailor the metal for your needs. Forms: - Granular
- Pigs
- Approx. 1 Lb. Regular Bars
- Sheet
- Cast Flat Anodes
- 1/4# Capping Bar
- Wire
- 2-5 Ingot
- 8-20 Mesh Shot
- Slabs
Belmont Product Code 7001 Nominal Composition: - 99.85 Sn
- Bal
-
For high speed and heavy load applications slightly softer than Grade 1. Forms: - 5-6 Ingot
- 1/8", 1/16", 1/32", 3/16", 5/32" Dia Solid Wire
- Pigs
Belmont Product Code 7881 Nominal Composition: - 89% Sn
- 7.5% Sb
- 3.5% Cu
Technical Info: - ASTM B-23 Grade # : 2
- Melting Point-Solidus : 241 C, 466 F
- Melting Point - Liquidus : 354 C, 669 F
- Pouring Temperature : 425 C, 795 F
-
This Solder has good corrosion resistance and tensile strength. With a melting range beginning at 390 Deg. F. it avoids causing damage to critical electronics as well preventing substrate deformation and segregation. It is used very often in spray wire form for capacitors and other electronic parts. Forms: - 1/16" Dia. Plus .000" Minus .004" on 5 Lb. Spools
- 2-5 Ingot
- Cast Flat Anodes
Belmont Product Code 7601DS1C Nominal Composition: - 60.5% Sn
- 39.5% Zn
-
Tin-Lead solders is the largest single group and the most widely used of the soldering alloys . Tin-Lead solders are compatible for use with all types of base metal cleaners, fluxes, and heating methods. 60/40 Tin Lead solder, almost the eutectic is particularly adaptable to delicate work or when soldering temperature may be critical. This particular item comes in 1/16" Diameter and can also be offered in other sizes as well. This is also a quick setting solder for fine electrical and tinsmith work. Forms: - 1/16" Dia. Solid Wire
Belmont Product Code 76001DSC Nominal Composition: - 60% Sn
- 40% Pb
-
This solder is primarily used for soldering Aluminum to Aluminum or Copper usually where lower soldering temperature than Zinc-Aluminum solders is required. It is used extensively in spray wire from for capacitors and other electronic parts and also has a high tensile strength. Forms: - 1/4" LB. Capping Bar
- 2-8 Ingot
- 2MM Dia. (.078" - .079") Wire
Belmont Product Code 7702 Nominal Composition: - 70% Sn
- 30% Zn
-
This is a Tin Base Babbitt for heavy load applications. Forms: - 5-6 Ingot
- 1/4" Dia. Solid Wire
- 1/8" Dia Wire
Belmont Product Code 7852 Nominal Composition: - 84% Sn
- 8% Sb
- 8% Cu
Technical Info: - ASTM B-23 Grade # : 3
- Melting Point-Solidus: 240 C, 464 F
- Melting Point - Liquidus: 422 C, 792 F
- Pouring Temperature: 490 C, 915 F
-
-
99.99% Pure Indium Shot it is most notably used in the semiconductor industry, in low melting-point metal alloys such as solders, soft metal high vacuum seals and in the production of transparent conductive coatings. Forms: - Ingot
- 1/4" and Down Shot
- Wire
- Bars
Belmont Product Code IN99AAA Nominal Composition: - 99.99% In
- Bal
-
This is a Bismuth based Eutectic low melting alloy used very often to bend tubes and rolled or extruded shapes. This alloy which is normally used for tubes up to 2-1/2" Diameter allows them to be bent or formed to the desired shape without any kinks. Without using this material the tubes or shapes may kink or bend irregularly. It can also be used for work-holding, fusible safety devices and low temperature soldering. Forms: - Cakes
- Capping Bars
- 1/8" & Down Shot
- .05", 1/8", 3/32" Dia Solid Wire
- 1/8" x 18" Cast Strips
Belmont Product Code 2505 Nominal Composition: - 50% Bi
- 10% Cd
- 26.7% Pb
- 13.3% Sn
Technical Info: - Melting Point - Solidus 158 F, 70 C
- Melting Point - Liquidus 158 F, 70 C
- Short-Term Tensile Strength lbs/sq.in. 5990
- Yield Temperature 158
- Weight lbs/cu.in 0.339
- Brinnell Hardness No. (500 kg) 9.2
- Growth/Shrinkage - Time after Casting: after 2 mi.: 0.0025
- after 1 hour: 0.0051
- after 24 hrs: 0.0051
- after 500 hrs: 0.0057
-
This is a Bismuth based Eutectic low melting alloy used for tooling and production aids. It provides you with easily castable material that is ready for use as soon as it freezes. This alloy can be recovered easily and recycled into new uses a number of times. It is mainly used in the optical industry for lens blocking when grinding glass, plastic lenses and optical components. It's low meeting point allows it not to distort the glass or plastic which it supports, Also can be used for proof casting as well. In comparison to its 117 Deg F. counterpart this alloy does not contain Cadmium. Forms: - 2 Lb. Cake Even Weight
- 1/8" Dia Solid Wire
- Capping Bars
Belmont Product Code 2491 Nominal Composition: - 49% Bi
- 18% Pb
- 21% In
- 12% Sn
Technical Info: - Melting Point - Solidus 136 F, 58 C
- Melting Point - Liquidus 136 F, 58 C
- Short-Term Tensile Strength lbs/sq.in. 6300
- Yield Temperature 136
- Weight lbs/cu.in 0.31
- Brinnell Hardness No. (500 kg) 14
- Growth/Shrinkage - Time after Casting: after 2 mi.: 0.0003
- after 1 hour: 0
- after 24 hrs: -0.0002
- after 500 hrs: -0.0002
-
This is a Bismuth based Eutectic low melting alloy used very often to bend tubes and rolled or extruded shapes. This alloy which is normally used for tubes greater than 2-1/2" Diameter allows them to be bent or formed to the desired shape without any kinks. With out using this material the tubes or shapes may kink or bend irregularly. It can also be used for work-holding, fusible safety devices and low temperature soldering. Forms: - Cakes
- 1/4# Capping Bar
- 1/8" Dia Solid Wire
- 10-20 Mesh
- 1-1/2 Lb. Regular Bars
- 40 Lb. Pigs
Belmont Product Code 2562 Nominal Composition: - 55.5% Bi
- 44.5% Pb
Technical Info: - Melting Point - Solidus 255 F, 124 C
- Melting Point - Liquidus 255 F, 124 C
- Short-Term Tensile Strength lbs/sq.in. 6400
- Yield Temperature 255
- Weight lbs/cu.in 0.38
- Brinnell Hardness No. (500 kg) 10.2
- Growth/Shrinkage - Time after Casting: after 2 mi.: -0.0008
- after 1 hour: -0.0008
- after 24 hrs: 0.0008
- after 500 hrs: 0.0022
-
This is a Bismuth based non-eutectic alloy commonly used as a low-melting solder and also to make custom shaped blocks. It is also used to make metal inlays in wood and also useful for repairing antiques as the low melting temperature of Wood's metal makes it unlikely this will harm the original piece. Forms: - 1/4" Dia. Solid Wire
- 1/8" Dia Solid Wire
Belmont Product Code 2502DS1C Nominal Composition: - 12.5% Sn
- 25% Pb
- 50% Bi
- 12.5% Cd
-
This is a Bismuth based non-eutectic alloy commonly used as a low-melting solder and also to make custom shaped blocks. It is also used to make metal inlays in wood and also useful for repairing antiques as the low melting temperature of Wood's metal makes it unlikely this will harm the original piece. Forms: - Capping Bars
- Cakes
- 1/4" Dia. Solid Wire
- 1/8" Dia Solid Wire
Belmont Product Code 2502 Nominal Composition: - 50% Bi
- 25% Pb
- 12.5% Sn
- 12.5% Cd
Technical Info: - Melting Point - Solidus 158 F, 70 C
- Melting Point - Liquidus 169 F, 76 C
- Short-Term Tensile Strength lbs/sq.in. 6100
- Yield Temperature 158
- Weight lbs/cu.in 0.347
- Brinnell Hardness No. (500 kg) 9.3
- Growth/Shrinkage - Time after Casting: after 2 mi.: -0.0001
- after 1 hour: 0.0002
- after 24 hrs: 0.0031
- after 500 hrs: 0.0035
-
This is a Bismuth based Eutectic low melting alloy whose main attribute is the minimal volume change between its liquid and solid state. This is the highest melting point of the bismuth-base alloys commonly used in the industry and provides an easily castable material ready for use soon after it freezes. It is used primarily for holding parts such as jet engine blades for machining and also for foundry patterns and fusible elements in safety devices. Forms: - Cakes
- .063" Dia. Solid Wire on 1 Lb. Spools
- 1/8" x 18" Cast Strips
- 1/8" X Down Shot
- 30 Lb. Pigs
- 5 lb. Ingot
Belmont Product Code 2581 Nominal Composition: - 58% Bi
- 42% Sn
Technical Info: - Melting Point - Solidus 281 F, 138 C
- Melting Point - Liquidus 281 F, 138 C
- Short-Term Tensile Strength lbs/sq.in. 8000
- Yield Temperature 281
- Weight lbs/cu.in 0.315
- Brinnell Hardness No. (500 kg) 22
- Growth/Shrinkage - Time after Casting: after 2 mi.: 0.0007
- after 1 hour: 0.0006
- after 24 hrs: 0.0005
- after 500 hrs: 0.0005
-
The principal uses of Cadmium are in low melting-point alloys and in the manufature of paint. Due to a low coefficient of friction and its resistance to fatigue, cadmium is often used in bearing and solder. It is also used extensively in electroplating, which accounts for about 60% of its use. Forms: - .79" Diameter Wire
- 1/4" Diameter Wire
- 1/8" Diameter Wire
- 3/16" Diameter Wire
- 3/32" Diameter Wire
Belmont Product Code 3006 Nominal Composition: - 99.95% Cd
- Trace
-
Lead Silver solders such as this have physical properties - tensile, creep, and shear strength - which are good to 350 Deg. F. Fatigue properties are also better than the non silver solder alloys. Forms: - .063 Dia. Solid Wire
- 5Lb. Spools
- Capping Bars
Belmont Product Code 5951DS1C Nominal Composition: - 60% Sn
- 40% Pb
- 5.5% Ag
-
This is a Bismuth based eutectic alloy which finds uses in shielding during medical radiation treatments and is also a cadmium-free solution for radiation therapy. This material also has a rapid growth of up to .0061 after casting. It has also been used as anchoring material and for designing fusible links. Forms: - Cakes
- 1/8", 1/32" Dia. Solid Wire
- Irregular Shot
- Pigs
Belmont Product Code 2531 Nominal Composition: - 52.5% Bi
- 32% Pb
- 15.5% Sn
Technical Info: - Melting Point - Solidus 203 F, 95 C
- Melting Point - Liquidus 203 F, 95 C
- Short-Term Tensile Strength lbs/sq.in. 6100
- Yield Temperature 203
- Weight lbs/cu.in 0.35
- Brinnell Hardness No. (500 kg) 9
- Growth/Shrinkage - Time after Casting: after 2 mi.: -0.0002
- after 1 hour: 0.0055
- after 24 hrs: 0.0057
- after 500 hrs: 0.0061
-
This is Bismuth based non-eutectic alloy which does not contract upon cooling. It is mainly used as a solder but also as a heat transfer medium. Another application for this material is to serve as a valve element in automatic fire sprinklers. The valve, having a low melting point, melts in fire and provides water to stop the fire from spreading. Forms: - 2 lb Cakes Even Weight
- 1/8" x 18" Cast Strips
- 1/16", 1/32" Dia. Solid Wire
- Approx. 1/2" x 6" x 12" Broken Slabs
Belmont Product Code 2503 Nominal Composition: - 50% Bi
- 25% Pb
- 25% Sn
Technical Info: - Melting Point - Solidus 203 F, 95 C
- Melting Point - Liquidus 239 F, 115 C
- Short-Term Tensile Strength lbs/sq.in. 6200
- Yield Temperature 203
- Weight lbs/cu.in 0.3365
- Brinnell Hardness No. (500 kg) 9.5
- Growth/Shrinkage - Time after Casting: after 2 mi.: -0.0001
- after 1 hour: 0.0045
- after 24 hrs: 0.0052
- after 500 hrs: 0.006